3816F
Product Name: 3816FProduct grade: Extruded film gradeProduct features: High-viscosity nylon 6 chips, with high strength and high modulus, meeting ROHS requirements.
Typical process
|
Dry |
Drum wind oven： 75～90℃，2～4h； Dehumidified dryer： 75～90℃，2～4h； Vacuum drying oven： 75～90℃，2～4h； |
|
Processing temperrature |
Feed section：220～230℃ Compressing section：235～255℃ Metering secion：230～250℃ |
|
Mold temperature optimum |
240℃ |
|
Processing Moisture Centent |
＜0.1% |
|
Test Item |
Test Standard |
Test Condition |
Unite |
Value |
|
Others |
||||
|
Product Identification |
ISO1043 |
—— |
—— |
PA6 |
|
Filler Content |
ISO3451-1 |
—— |
% |
0 |
|
Density |
ISO1183 |
23℃ |
g/cm³ |
1.13±0.02 |
|
Melt Flow Rate |
ISO 1133 |
275℃，2.16kg |
g/10min |
8 |
|
Relative Viscosity |
ISO307 |
96%H2SO4,1g/dl |
ml/g |
4.05±0.05 |
|
Viscosity number |
ISO307 |
96%H2SO4,0.5g/dl |
ml/g |
245±10 |
|
Extractables |
ISO6427 |
—— |
% |
≤0.5 |
|
Impurities、Different color particles |
—— |
Visual inspection |
Grain/g |
≤1 |
|
Mechanical |
||||
|
Flexural Strength |
ISO178 |
23℃，2mm/min |
MPa |
110 |
|
Flexural Modulus |
ISO178 |
23℃，2mm/min |
MPa |
2200 |
|
Tensile Strength |
ISO527 |
Type I spline,50mm/min |
MPa |
70 |
|
Tensile Module |
ISO527 |
Type I spline,1mm/min |
MPa |
2500 |
|
Tensile Strain at Break |
ISO527 |
Type I spline,50mm/min |
% |
110 |
|
Charpy Notched Impact Strength |
ISO179/1eA |
23℃ |
kJ/m2 |
6/C |
|
Charpy Unnotched Impact Strength |
ISO179/1eU |
23℃ |
kJ/m2 |
60/N |
|
Rockwell Hardness |
ISO2039-2 |
R Scale |
— |
65 |
|
Thermal |
||||
|
Melting Temperature |
ISO11357 |
—— |
℃ |
220±5 |
|
Heat Distortion Temperature |
ISO75-2 |
0.45MPa |
℃ |
105 |
|
1.8MPa |
℃ |
/ |
||
|
Electrical |
||||
|
Volume Resistivity |
IEC60093 |
—— |
Ω•cm |
1015 |
|
Surface resistivity |
IEC60093 |
—— |
Ω |
1013 |
All is typical data, only for reference, not the permit of quality assurance.
Related products
-
The product should be stored sealed in a light-proof and dry place at a storage temperature of 2 – 8 degrees Celsius. Under these conditions, the shelf life is 1 year.
-
Hydroxypropyl acrylate is extensively utilized in the production of inks, radiationcurable products,high-solids coatings,powder coatings,water-soluble resins, paper processing agents.
-
Adhesives, rubber compounds & Concrete superplasticizers
-
CAS: 91973-93-2 Product Name: (6-Oxo-3-phenylpyridazin-1(6H)-yl)acetic acid
-
Silicone defoamers use dimethyl silicone oil, silica, etc., as active ingredients, compounded with various emulsifiers.
Reviews
There are no reviews yet.