316L Stainless Steel Plate
316L stainless steel has a lower proportion of carbon in its composition. To qualify as 316L stainless steel, the amount of carbon cannot exceed 0.03%.
Product Parameters
|
Product Name |
316L Stainless Steel Plate |
|
Type |
Plate |
|
Thickness |
0.3mm-200mm |
|
Length |
2000mm, 2438mm, 3000mm, 5800mm, 6000mm, 12000mm, etc. |
|
Width |
40mm-600mm, 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc. |
|
Standard |
ASTM, AISI, JIS, GB, DIN, EN, etc. |
|
Surface |
BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc. |
|
Scope of Application |
Widely used in high temperature and electrical industry, medical equipment construction, chemical, food industry, agriculture and ship parts, food and beverage packaging, Kitchen supplies, trains, airplanes, conveyor belts, vehicles, bolts, nuts, springs and screens, etc. |
|
Certificate |
ISO, SGS, BV, etc. |
|
Production Technology |
Hot Rolling, Cold Rolling |
|
Edge Processing |
Edging, Trimming |
Chemical Composition
|
C |
Si |
Mn |
Cr |
Ni |
S |
P |
Mo |
|
≤ 0.03 |
≤1.0 |
≤ 2.0 |
16.0～18.0 |
10.0～14.0 |
≤ 0.03 |
≤ 0.045 |
2.0～3.0 |
Mechanical Properties
|
Tensile Strength Kb (MPa) |
Yield Strength σ0.2 (MPa) |
Elongation D5 (%) |
Hardness |
|
≥480 |
≥177 |
≥ 40 |
≤ 187HB;≤ 90HRB;≤ 200HV |
Physical Performance
|
Density(g/cm³) |
Modulus of Elasticity(Gpa) |
Coefficient of Thermal Expansion(10-6/°C) |
Coefficient of Thermal Conductivity(W/m*K) |
Resistivity(ΜΩ. cm) |
|
7.99 |
193 |
16.0 |
16.2 |
74 |
Surface Selection
Related products
-
309 stainless steel is a stainless steel type with incredible corrosion resistance and high temperature performance. It is widely used in fields such as aviation, chemical industry, and petroleum.
-
1070 belongs to the pure aluminum series alloys. The aluminum content is greater than 99.7%, and the content of other impurity elements is low.
-
304L stainless steel is remarkably similar to 304 stainless steel in their chemical composition with one key difference.
-
316L stainless steel has a lower proportion of carbon in its composition. To qualify as 316L stainless steel, the amount of carbon cannot exceed 0.03%.
-
310S stainless steel is austenitic chromium-nickel stainless steel, with good oxidation resistance, corrosion resistance
Reviews
There are no reviews yet.