BG3SI21
Product Name: PA6-GF15Product grade: Injection molding gradeProduct features: 15% glass fiber reinforced nylon 6, with excellent surface finish, meeting ROHS requirements.
Typical molding process
|
Dry |
Drum wind oven： 100～120℃，4～6h； Cycling warm air： 100～120℃，4～6h； Vacuum drying oven： 100～120℃，3～4h； |
|
Processing temperrature |
Feed section：225～240℃ Compressing section：240～270℃ Metering secion：240～270℃ |
|
Injection pressure |
70～130MPa |
|
Packing pressure |
40～90 MPa |
|
Mold temperature |
70～100℃ |
|
Back pressure |
8～15MPa |
|
Test Item |
Test Standard |
Test Condition |
Unite |
Value |
|
Others |
||||
|
Product Identification |
ISO1043 |
—— |
—— |
PA6-GF15 |
|
Filler Content |
ISO3451-1 |
—— |
% |
15 |
|
Density |
ISO1183 |
23℃ |
g/cm³ |
1.20 |
|
Molding shrinkage(parallel/ normal) |
ISO 294-4 |
—— |
% |
0.3/0.8 |
|
Melt Flow Rate |
ISO 1133 |
250℃，2.16kg |
g/10min |
20 |
|
Mechanical |
||||
|
Flexural Strength |
ISO178 |
23℃，2mm/min |
MPa |
155 |
|
Flexural Modulus |
ISO178 |
23℃，2mm/min |
MPa |
4500 |
|
Tensile Strength |
ISO527 |
Type I spline,50mm/min |
MPa |
110 |
|
Tensile Module |
ISO527 |
Type I spline,1mm/min |
MPa |
5500 |
|
Elongation at Break |
ISO527 |
Type I spline,50mm/min |
% |
5.5 |
|
Charpy Notched Impact Strength |
ISO179/1eA |
23℃ |
kJ/m2 |
10 |
|
Charpy Unnotched Impact Strength |
ISO179/1eU |
23℃ |
kJ/m2 |
65 |
|
Thermal |
||||
|
Melting Temperature |
ISO11357 |
—— |
℃ |
220 |
|
Heat Distortion Temperature |
ISO75-2 |
0.45MPa |
℃ |
205 |
|
1.8MPa |
℃ |
190 |
||
|
Electrical |
||||
|
CTI |
IEC60112 |
A |
V |
/ |
|
Volume Resistivity |
IEC60093 |
—— |
Ω•cm |
1013 |
|
Surface resistivity |
IEC60093 |
—— |
Ω |
1012 |
|
Flammability |
||||
|
Flammability |
UL-94 |
1.6mm |
Class |
HB |
All is typical data, only for reference, not the permit of quality assurance.
Related products
-
CAS: 91973-93-2 Product Name: (6-Oxo-3-phenylpyridazin-1(6H)-yl)acetic acid
-
Adhesives, rubber compounds & Concrete superplasticizers
-
Silicone defoamers use dimethyl silicone oil, silica, etc., as active ingredients, compounded with various emulsifiers.
Reviews
There are no reviews yet.